[230]Effects of Initial Crystallographic Orientation of Grains on the Formation of Deformation Twins in a Cu-Zn Alloy

*Yanshuo Li¹, Chihiro Watanabe², Norimitsu Koga², Hiromi Miura³ (1. Kanazawa Univ. (Graduate Student), 2. Kanazawa Univ., 3. Toyohashi Univ. Tech.)

Cu-Zn alloy,Crystallographic orientation,Deformation twin,Cold rolling

板面法線方向に<001>が強く集積したCu-Zn合金を用いて，変形双晶形成に及ぼす圧延方向（RD）の結晶方位依存性の調査を行った．RDの結晶方位に依存して，変形双晶の形成頻度が異なる事がわかった．