[P72]Tailoring Deformation Pathways in Ni-Free ODS Austenitic Alloys for Strength–Ductility Optimization under Ambient and Elevated Temperatures toward Nuclear Fusion Applications

*Diancheng Geng1, Rama Varanasi1, Zimo Gao1,2, Kota Mizuguchi1,2, Minha Park1, Yasuyuki Ogino1, Hao Yu1, Sosuke kondo1, Koji Inoue1, Akira Hasegawa1, Junichi Miyazawa3, Motomichi Koyama1, Ryuta Kasada1 (1. IMR, Tohoku Univ., 2. Graduate School of Engineering, Tohoku Univ., 3. Helical Fusion Co., Ltd.)

Keywords:

Oxide-dispersion strengthened austenitic alloys,Twinning-induced plasticity,Strength-ductility balance

Niを含む従来型ODSオーステナイト合金に代わる低放射化型ODS合金を設計しました。本合金は高温力学特性を維持しつつ、室温では双晶誘起変形により優れた強度–延性バランスを示しました。