[J10]Hardening and embrittlement in Ti-10Mo air-cooled after annealing

*Xiuqun Wang1, Chong Yan2, Reza Gholizadeh2, Nobuhiro Tsuji2 (1. Graduate School of Materials Science & Engineering, Kyoto University, Kyoto, Japan、2. Department of Materials Science & Engineering, Kyoto University, Kyoto, Japan)

Keywords:

Metastable β-Ti alloy,Hardening,Embrittlement,Omega,Cooling rate

Ultrahigh yield strength is achieved in Ti-10Mo alloy air-cooled after annealing, accompanied by a great loss of ductility, which is further discussed by considering α phase and ω nano-precipitates.