[249] Linear friction welding of Haynes 282 Ni superalloy

○Abhishek SHARMA¹, Yasuhiro Aoki¹, Yoshiaki Morisada¹, Kohsaku Ushioda¹, Hidetoshi Fujii¹ (1. JWRI, The University of Osaka)

キーワード：

Linear friciton welding (LFW)、Haynes 282、Ni Superalloy、Solid state joining

The linear friction welding (LFW) of Haynes 282 Ni superalloy is performed at different applied pressures of 100, 300, and 500 MPa, with a constant oscillation frequency and amplitude. 100 % Joint efficiency is achieved in as-weld and PWHT conditions for 300 and 500 MPa specimens with base metal fracture.