[3G13] Feasibility Study of Integral Molten Chloride Salt Fast Reactor (IV)(8) Research trial about compatibility under Ni ion irradiation on Ni-based alloy with chloride salt

*Daiki Takebayashi¹, Ken-ichi Fukumoto¹, Yuji Arita¹, Ryoya Ishigami² (1. Univ. of Fukui, 2. WERC)

Keywords:

Molten Salt,Ion Irradiation,Corrosion,Ni-based Alloy

In order to investigate the irradiation microstructure of Hastelloy alloys, corrosion tests using chloride eutectic salts were performed on Ni-self-ion irradiated Hastelloy-C276,N. We obtained knowledge about the change of irradiation defects before and after corrosion and the Loss of mass due to the introduction of irradiation defects.