[1G13]Development of FeCrAl-ODS alloy for BWR accident tolerant fuel cladding tubes(2) Effect of trace added element Ti on corrosion and high-temperature oxidation properties

*KAN SAKAMOTO1, Yusuke Miura1, Junji Matsunaga2, Hajime Miyata3, Masana Sasaki4, Kenichi Yasuda4, Naoko Oono5 (1. NFD, 2. GNF-J, 3. Hitachi GE Vernova (Current: NFD), 4. Hitachi GE Vernova, 5. Yokohama Natl. Univ. (Current: Tohoku Univ.))

Keywords:

ATF,FeCrAl-ODS alloy,Corrosion,High-temperature oxidation