[9p-S5-8] Laser-shock-induced nanodiamond formation from polyethylene terephthalate

〇(D)Kai Taketoshi¹, Daisuke Murayama¹, Alexis Amouretti¹, Ryosuke Furukawa¹, Hirotaka Nakamura¹, Yusuke Nakanishi¹, Akane Oyama¹, Naoki Yamagata¹, Kohdai Yamamoto¹, Ryosuke Kodama^1,2, Kohei Miyanishi^2,3, Makina Yabashi^3,4, Toshinori Yabuuchi^3,4, Yusuke Seto⁵, Micheal Stevenson⁶, Dominik Kraus⁶, Philipp May⁶, Jonas Kuhlke⁶, Marie-Luise Herbert⁶, Julian Lutgert⁶, Francesco Barbato⁶, Alessandra Ravasio⁶, Johannes Rips⁶, Samuel Schumacher⁶, Feng Xiaokang⁶, Bjom Lindqvist⁶, Dirk Frundt⁶, Lennart Konig⁶, Norimasa Ozaki^1,2 (1.Grad. School of Eng., The Univ. of Osaka, 2.ILE, The Univ. of Osaka, 3.RIKEN, 4.JASRI, 5.Osaka Metropolitan Univ., 6.Rostock Univ.)

Keywords:

Laser-shock,Nanodaiamond,X-ray diffraction

PETはレーザーショック圧縮下でナノ粒子上のダイヤモンド（ナノダイヤモンド）を形成する。本研究では、その場X線回折により、レーザーショック圧縮下でのナノダイヤモンド形成の時間進展を圧縮開始直後から圧力解放後十数ナノ秒まで計測した。ナノダイヤモンドは圧縮開始後3ナノ秒から観測可能になり、圧力解放後1ナノ秒までは増加したが、その後は緩やかに減少し、最終的にはダイヤモンド信号は観測されなくなった。