[63] Corrosion Protection of Al Alloy by Molybdate-Loaded Layered Double Hydroxide Coatings through Electrophoretic co-Deposition

○Supicha Trakuldit^1,2, Sachiko Hiromoto^2,1, Kotaro Doi² (1. Waseda Univ., 2. NIMS)

キーワード：

Corrosion Protection、Aluminum Alloy、Layered double hydroxide

MoO₄^2--intercalated LDH coatings were fabricated on A6061 by electrophoretic co-deposition. The coatings preferentially formed on intermetallic precipitates, reducing cathodic oxygen reduction. Release of MoO₄^2- from LDH was confirmed after corrosion, producing superior corrosion resistance through physical barrier and inhibitor effects.